RAL5015 Thermosetting Powder Paint
RAL5015 Thermosetting Powder Paint
RAL5015 Thermosetting Powder Paint is made by using high quality polyester and TGIC. It has various products such as high light, half light, metal effect, art, wrinkles and so on.
The powder coating has excellent weather resistance and chemical resistance, high mechanical strength and tenacity of coating.
Surface coatings for electrical equipment, heating and ventilation equipment, iron wheels, automobile spare parts, agricultural machinery, engineering machinery, office equipment, air conditioners, external decoration materials, mobile houses and other exposed facilities.
| RAL5015 Thermosetting Powder Paint | ||
| Product Profile | Cp-05 thermosetting polyester powder coating is made of special polyester, special curing agent and additives. This product does not contain TGIC, more in line with environmental requirements. Varieties of high light, half light, matte, metal effect, art, wrinkles and other color products. | |
| Characteristic | The coating has excellent weather resistance and chemical resistance, high mechanical strength, tough film and excellent weather resistance. | |
| Applicability | Surface coating of outdoor exposed facilities such as aluminum profile, electrical equipment, heating and ventilation equipment, iron wheel, automobile spare parts, agricultural machinery, engineering machinery, office equipment, air conditioner, expressway guardrail, external decoration materials, movable house, etc. | |
| Theoretical coverage | 10-12㎡/kg，（Film thickness 60 ų ṃ, with the state of the workpiece, coating method, coating conditions, all the differences） | |
| Dry storage stability | 12 months (less than 30 ℃) | |
| Pretreatment | Aluminum: according to the ISO / din50939 standard, the aluminum material is pretreated with yellow chromate or green chromate. It is recommended to use deionized water for the last water cleaning, and dry in the drying furnace at no more than 90 ℃ to ensure the best adhesion and achieve the best durability. Steel plate: chromate or zinc phosphating. It is suggested that the best protection should be given to the former drug suppliers. Galvanized sheet: phosphating with zinc chromate. In order to avoid pinholes in the cured coating caused by tiny bubbles, preheating is recommended. | |
| Curing process | 1. Low temperature curing 160 ℃ @ 25min (MT) | |
| 2. Conventional curing 180 ℃ @ 15min (MT) | ||
| 3. Rapid curing 200 ℃ @ 10min (MT) | ||
| Construction method | Electrostatic and friction gun spraying, manual and automatic. Metal flash powder can only be applied with electrostatic coating, and arts and crafts powder is recommended to use automatic gun spraying to ensure uniform color and appearance effect. | |
| Main technical specifications | ||
| Item | Test standard | Index |
| Gardner60 º gloss | ASTMD523,ISO2813，GB/T9754-18 | Gloss between 10-95% as per customer requirements |
| Scribble adhesion | ASTMD3359,ISO2409，GB/T1185-98 | Grade 0 |
| Bending test of shaft bar | ASTMD522,ISO1519 | 3mm |
| Impact resistance | AS3715 2.8,GB/T1732-93 | 30-50kg.cm |
| Cupping test | ISO1520，GB/T9753 | 4-7MM |
| Pencil hardness | GB/T6739-98 | 1H-2H |
| Salt fog resistance | ASTMB117-87,GB/T1771-91 | The maximum scratch corrosion after 600H test is 1mm |
| Heat and humidity resistance | ASTMD2247-87,GB/T17740-89 | After 600h, the coating has no effect on the light loss |
| QUV artificial accelerated aging | 600h | No powdering, light retention > 50%, color change less than munsel1 |
| Resistant to 10% HCI | 240h | No bubbles, no surface damage |
| Resistant to 10% NaOH | 240h | No bubbles, no surface damage |
| Can be customized according to customer requirements | ||
Product Tag: